Aromatic and rigid rod polyelectrolytes based on sulfonated poly(benzobisthiazoles)

Abstract

Aromatic polyelectrolytes based on sulfonated poly(benzobisthiazoles) (PBTs) have been synthesized by a polycondensation reaction of sulfo-containing aromatic dicarboxylic acids with 2,5-diamino-1,4-benzenedithiol dihydrochloride (DABDT) in freshly prepared polyphosphoric acid (PPA). Several sulfonated PBTs, poly[(benzo[1,2-d : 4,5-d']bisthiazole-2,6-diyl)-2-sulfo-1,4-phenylene] sodium salt (p-sulfo PBT), poly[(benzo[1,2-d : 4,5-d]bisthiazole-2,6-diyl)-5-sulfo-1,3-phenylene] sodium salt (m-sulfo PBT), their copolymers, and poly[(benzo[1,2-d : 4,5-d']bisthiazole-2,6-diyl)-4,6-disulfo-1,3-phenylene] potassium salt (m-disulfo PBT), have been targeted and the polymers obtained characterized by 13 C-NMR, FT-IR, elemental analysis, thermal analysis, and solution viscosity measurements. Structural analyses confirm the structures of p-sulfo PBT and m-disulfo PBT, but suggest that the sulfonate is cleaved from the chain during synthesis of m-sulfo PBT. m-Disulfo PBT dissolves in water as well as strong acids, while p-sulfo PBT dissolves well in strong acids, certain solvent mixtures containing strong acids, and hot DMSO. TGA indicates that these sulfonated PBTs are thermally stable to over 500°C. Free-standing films of p-sulfo PBT, cast from dilute neutral DMSO solutions, are transparent, tough, and orange in color. Films cast from basic DMSO are also free standing, while being opaque and yellow-green. p-Sulfo PBT was incorporated as the dopant ion in polypyrrole, producing conductive films with conductivities as high as 3 S/cm and electrical anisotropies as high as 10.