Abstract
ABSTRACTMicrowrinkles were formed by treating poly(dimethylsiloxane) (PDMS) surfaces with a mixture of concentrated sulfuric acid and nitric acid at 80 °C followed by a water rinsing step. The acid treatment oxidized the treated area, which also swelled owing to absorption of water during the rinsing step. This absorption of water induced a compressive stress on the PDMS surface that caused the formation of wrinkles. The appearance of wrinkles was controlled by the time interval between the end of the acid treatment and the beginning of the water rinsing step. Wrinkles were formed when the time interval was shorter than 5 s, as water was absorbed by the hygroscopic acid molecules within the treated surface. For longer time intervals of 300 s, this phenomenon was not observed. Based on these findings, a procedure for forming wrinkles in specific areas was developed by hydrating the chosen areas with wet filter paper cut into specific shapes after the acid treatment. The formation of wrinkles was confined to the area under the piece of paper. The orientation and alignment of the wrinkles at the boundaries were also characterized. © 2014 Wiley Periodicals, Inc. J. Polym. Sci., Part B: Polym. Phys. 2015, 53, 167–174
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callMore From: Journal of Polymer Science Part B: Polymer Physics
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.