Abstract
ZIF-8 films were prepared on both sides of nylon membrane in aqueous solutions using a stoichiometric ratio of Zn2+ and 2-methylimidazole (hmim) by a contra-diffusion method. Both ammonium hydroxide solution and porous nylon membrane play a crucial role in promoting ZIF-8 crystallization and film formation. Ammonium hydroxide solution added in the hmim solution deprotonates hmim, and the nylon membrane separates the Zn2+ and hmim aqueous solutions with different diffusion rates through its pores, leading to appropriate concentration gradients of hmim and zinc nitrate required for ZIF-8 nucleation and growth. The synthesis conditions were systematically investigated. ZIF-8 films prepared with a Zn2+:hmim:NH4+ molar ratio of 1:2:32 at room temperature for 24h exhibited an intergrown ZIF-8 layer on hmim side with a thickness of ca. 2.5μm, and gas permeation confirmed the film was continuous and compact with a H2/N2 ideal selectivity of 4.6.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.