Abstract
CaO nanoparticles have been prepared using CaCl2 and aqueous extract of broccoli as a precursor and reducing agent, respectively. Different volumes of the aqueous broccoli extract were utilised to obtain Ca(OH)2 and subsequent calcination gave CaO nanoparticles. The synthesised CaO was confirmed by powder X-ray diffraction (XRD). The morphology was studied using transmittance electron microscopy (TEM), and the surface composition of Ca(OH)2 was explored using Fourier transform infrared spectroscopy. The major functional groups present in the capping material responsible for the reduction of the metal salt and the surface passivation of Ca(OH)2 were identified. The XRD pattern revealed cubic phase for all the CaO nanoparticles, and the crystallite size was estimated using Scherrer's equation showed a variation which is dependent on the volume of the extract used. TEM analysis showed different shapes, while the selected area electron diffraction (SAED) results confirmed the crystallinity of the nanoparticles. Thermogravimetric analysis of Ca(OH)2 showed the decomposition product to be CaO. Sample C3, which has the smallest particle size, was used as a catalyst for the degradation of bromocresol green via photo irradiation with ultraviolet light and the result revealed a degradation efficiency of 60.1%.
Published Version
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.