Abstract
Strontium surface segregation is the main issue that causes long-term performance degradation in strontium-containing electrodes for solid oxide electrolysis cells. In this research, we effectively suppress strontium segregation by applying an anodic current that drives the segregated strontium back to the perovskite lattice and mitigate electrode performance degradation. By monitoring the impedance of Sr2Fe1.5Mo0.5O6-δ (SFM) air electrode under open circuit voltage at high temperature with changing current densities over time, the degradation caused by strontium segregation is verified. The applied current successfully prevent the polarization resistance from increasing is observed. The cell with 0.8 A/cm2 of the applied current increase only 3% of polarization resistance as compared to the cell without applied current after testing at 800 ℃ for 24 h. The atomic ratio of strontium on the SFM electrode surface shows lower strontium content after undergoing applied current, which means that the strontium is indeed migrated back to perovskite lattice under the applied current and result in slower degradation of the SFM electrode.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.