Abstract
Polymeric “rejection enhancing agents” (REAs) were shown to form rather durable coatings, on flat sheet polyamide membranes, thereby sealing defects for improved salt rejection performance. Dilute solutions of three REAs, i.e. Polyvinyl methyl ether (PVME), polyvinyl pyrrolidone (PVP) and polyvinyl alcohol (PVA), followed by tannic acid, were tested on two types of low-pressure reverse osmosis membranes. PVA and PVP have a significant advantage over PVME, as they do not exhibit cloud point limitations at elevated feed-water temperatures. Treatment in dead-end mode of an unused membrane (A), with REAs concentrations 5 ppm to 30 ppm, led to significant rejection improvement and guided subsequent experiments. Emphasis was placed on performance restoration of a used degraded membrane (B2). In dead-end and cross-flow tests with this membrane, there was significant rejection improvement, with a modest concurrent flux reduction; best results were obtained with REAs applied at concentration 10 ppm and pressure 1034 kPa (150 psi), over a 30 min period. Additionally, when the initial salt rejection of a membrane sample was low (possibly due to active layer degradation) the treatment resulted in the greatest rejection improvement. Successful online treatment with REAs in a cross-flow experimental system, without interrupting normal operation, suggests that the process is attractive for practical applications.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.