Abstract
The effect of bias voltages (40 V, 80 V, and 40/60/80 V) on microstructure and electrochemical properties of arc-PVD CrN coatings were evaluated. Increasing the bias voltage produced microstructural changes, from well-defined columns to columnar grains, and increased defect size. The electrochemical response proved susceptible to the defect type. Nano-droplets promoted the formation of oxides, while large pores allowed the migration of the electrolyte to the substrate/CrN interface. An impedance equivalent circuit based on the Bisquert transmission line was proposed to fit the experimentally obtained impedance spectra. The equivalent circuit allowed correlating the coating electrochemical response to the defect densities and sizes. Samples deposited with 40 V showed the lowest corrosion current (0.05 μA/cm2 ± 0.01), which was supported by the highest resistances to the transport of ions through the pores (Rp = 1047 ± 88 kΩꞏcm2). Films obtained with 80 V reduced Rp values by two magnitude orders compared to CrN 40 V. The increase of pore resistance in CrN 40 V was associated with the oxidation of nano-droplets (proposed auto-protection phenomenon), which blocks open pinholes due to the smallest average size of defects. Tailoring a gradual increase of the bias voltage (40/60/80 V) preserves the auto-protection mechanism of droplets and improves the surface finish of the coating.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.