Applicability of Miniature C(T) Specimens for the Master Curve Evaluation of RPV Weld Metal

Abstract

The Master Curve approach for the fracture toughness evaluation is expected to be a powerful tool to ensure the reliability of long term used reactor pressure vessel (RPV) steels. In order to get sufficient number of data for the Master Curve approach coexistent with the present surveillance program for RPVs, the utilization of miniature specimens that can be taken from the broken halves of the surveillance Charpy specimens is important. CRIEPI has developed the test technique for the miniature C(T) specimens, whose dimensions are 4 × 10 × 9.6 mm, and has verified the basic applicability of the Master Curve approach by means of the miniature C(T) for the determination of the fracture toughness of typical Japanese RPV steel base metals [1]. A series of round robin tests on RPV steel base metals [2–4] demonstrated that the miniature C(T) specimen can be used for the determination of the reference temperature (To) with no specific difficulties in test techniques. The present paper addresses the applicability of the fracture toughness evaluation by the miniature C(T) specimens on a RPV weld metal with multi-layer weld bead structure. The distribution of the fracture toughness and the trend in fracture toughness change with temperature were confirmed to show a good agreement with the assumption of the Master Curve method [5]. Fracture surface of the specimens were in cleavage fracture mode regardless of the difference in fracture toughness level. The relevance of the specimen size correction in the Master Curve method was confirmed. The difference of To values were only in a few degrees Celsius between the data obtained with 0.5 inch-thickness C(T) specimens and the miniature C(T) specimens. The effect of local loss of constraint nearby the specimen side surface was examined by comparing with the datasets from the specimens with and without side grooves. The difference of To was only 3 degree centigrade and no remarkable effect of side grooving could be seen. From overall examination results, it was concluded that the miniature C(T) specimen can be used for the Master Curve evaluation of tested PRV weld metal.