Abstract
Cellulose and chitosan are natural polymers that have been used as biocomposite. The aim of this research is to obtain biofilms from chitosan and oxidized cellulose crosslinks. This research is divided into three steps, i.e., isolation of cellulose from oil palm trunk and oxidation of cellulose using NaIO4 (0.2; 0.4; 0.6; 0.8; 1.0 mg/mL) to obtain dialdehyde cellulose (DAC), crosslink of oxidized cellulose with chitosan (DD = 72.85%) to obtain biofilm of chitosan/DAC (CDAC), and characterization of biofilms. The crosslinked reaction was confirmed by FT-IR analysis that showed the spectrum of Schiff base C=N group at 1651 cm–1. Tensile strength increased gradually when the NaIO4 concentration used was 0.2–0.6 mg/mL, but after those concentrations, the tensile strength slightly decreased. The morphology analysis showed that CDAC had smoother morphology than DAC, which was shown rough and showed some particle indicated the presence of unreacted cellulose. CDAC biofilms that prepared with 1.0 mg/mL NaIO4 showed the greatest antibacterial activity.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.