Abstract
Infection following surgery can result in significant pain and morbidity for patients undergoing vertebroplasty/kyphoplasty, and often results in revision surgery. This study focuses on the development of Al-free glass polyalkenoate cements (GPCs) based on 0.04SrO-0.12CaO-0.36ZnO-0.48SiO( 2) glass, with the intent of optimizing their antibacterial efficacy by incorporating low-molecular-weight polyacrylic acids (PAA) and trisodium citrate (TSC), and evaluating the resultant GPCs against bacteria relevant to spinal infections, P. aeruginosa and E. coli. Ion-release profiles were determined for the GPC formulation containing E6 PAA (Cement A) and E7 PAA (Cement B), and Zn, Na, and Sr release was recorded over 1, 7, and 30 days. Inhibition was found in E. coli at each time period (0-30 days) and this generally decreased with exposure time in water. The largest GPC inhibition zones were produced by Cement A (6 mm); however the control material Simplex P + tobramycin produced much higher inhibition zones (11 mm). When testing the GPC against P. aeruginosa, inhibition was only present at the 0-day time period. Simplex P + tobramycin was found to produce inhibition at each time frame. Analysis of the agar from the inhibition zone of the E. coli test revealed that there is a significant change in Zn concentration as compared to a control agar specimen, which suggests that Zn release is responsible for the antibacterial effect of the GPCs.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.