Abstract
DSC was used for heat capacity measurements of pure RuO2 in the temperature range from 300 to 1170 K of solid solutions corresponding to the compositions of (Ti1−x Rux )O2 (x ≤0.15 and x ≥0.85) and in the temperature range from 300 to 1550 K of pure TiO2. The analysis of experimental data obtained within ±2% of accuracy has shown that the characteristic temperatures representing the harmonic lattice vibrations do not strongly depend on the chemical composition x . It was demonstrated that non-harmonic heat capacity is strongly correlated to x. The existence of additional excess heat capacity was observed with the mixed oxide solid solution samples of low Ru content and explained by the defect formation model.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.