Abstract
Glassy metallic Hf thin films were obtained using electron beam deposition at room temperature due to the low energy received by Hf atoms during the film formation process. The amorphous nature of the Hf films suggested by XRD was confirmed by low temperature electrical conductivity measurements where a negative temperature coefficient of resistivity was identified. Anodic oxidations using a scanning droplet cell microscopy were performed on a typical crystalline (hexagonal) Hf film obtained by sputtering and on the glassy Hf. A decrease of the oxide formation factor by 30% (from 2.4 to 1.7 nm V−1) was evidenced on the amorphous Hf. Electrochemical impedance spectroscopy on both samples revealed almost identical capacitances while the electrical permittivities were found to differ by 40%. The dielectric constant of the HfO2 decreased from 33.5 on the crystalline parent metal sample to 19.8 on the amorphous one. The unexpected 10% deviation was attributed to a smoother defect-free oxide/metal interface in the case of HfO2 grown on glassy Hf film.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.