We demonstrated the successful water treatment performance of a continuous-flow tubular TiO2 nanotube reactor made of Ti pipe where a TiO2 nanotube (TNT) layer was directly formed on the inner wall by an electrochemical anodization process. A cylindrical UV lamp was inserted into the pipe to irradiate the inner TNT surface as a light source. To optimize the thickness of TNT layer on Ti pipe, TNT layers with 1, 5 and 10μm thickness were prepared and their photocatalytic activities were tested for the degradation of various organic substrates (acid orange 7 (AO7), dichloroacetate (DCA), and 4-chlorophenol (4-CP)) under UV illumination. The TNT layer with 10μm thickness showed the highest photocatalytic activity, with first-order removal rate constants (k:min−1) of 0.019, 0.039, and 0.025 for AO7, 4-CP, and DCA, respectively. The directly formed TNTs (10μm thickness) on Ti pipes in the continuous-flow tubular TNT reactor, having a strong adhesiveness and a high surface area, enabled the successful degradation of organic compounds and to have kept the activity without decrease during the repeated cycles and long-term experiments. The photocatalytic performance of the tubular TNT reactor was tested with a higher concentration, smaller volume ([4-CP]0=100μM, solution vol.=15mL) and a lower concentration, larger volume ([4-CP]0=20μM, solution vol.=100mL) in the circulation-flow mode (20mLmin−1). A good performance was achieved under the low intensity UV illumination (≈2mWcm−2) with a half-life of ca. 50min and ca. 11h with 80% and 79% removal of TOC for the above two test conditions, respectively. The proposed tubular TNT reactor can be an effective option in the design of continuous flow-type photocatalytic reactors for practical water purification.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.