Abstract
This study evaluated the surface optimization of β-Ti-40Nb alloy in terms of corrosion and bioactivity properties. Electrochemical anodization at different voltages was used to synthesize (Ti,Nb)O2 nanostructures (nanopores (NPs)) and (nanotubes (NTs)) on samples' surfaces, allowing the analysis of their influence on performances related to those properties. Then, (Ti,Nb)O2 NPs and NTs were annealed at 550 °C to crystallize the previously obtained amorphous (Ti,Nb)O2 into a mixture of anatase and rutile. Also, a pre-calcification process (PC) was applied on annealed (Ti,Nb)O2 NPs and NTs. SEM micrographs showed the presence of NTs (10 V) and NPs (20 V) after anodization. After annealing, the morphology of (Ti,Nb)O2 NPs and NTs remained constant for both diameter and length. XRD analysis confirmed that as-anodized amorphous (Ti,Nb)O2 was crystallized, after annealing, into a mixture of anatase-rutile phases. Corrosion properties were evaluated through the open circuit potential (OCP), potentiodynamic polarization curves, and electrochemical impedance spectroscopy (EIS). Samples were immersed in a simulated body fluid (SBF) solution for one to 14 days to assess the bioactivity. The bioactivity evaluation was carried out by mass gain. Also, the amount of apatite precipitated on the sample's surface was determined through SEM-EDS. The results showed that PC samples presented similar corrosion properties compared to the annealed samples. However, PC processing improved the bioactivity (apatite formation) of (Ti,Nb)O2 NTs and NPs modified β-Ti-40Nb alloy.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.