Abstract
Although surface terminations (such as ═O, -Cl, -F, and -OH) on MXene nanosheets strongly influence their functional properties, synthesis of MXenes with desired types and distribution of those terminations is still challenging. Here, it is demonstrated that thermal annealing helps in removing much of the terminal groups of molten salt-etched multilayered (ML) Ti3C2Tz. In this study, the chloride terminations of molten salt-etched ML-Ti3C2Tz were removed via thermal annealing at increased temperatures under an inert (argon) atmosphere. This thermal annealing created some bare sites available for further functionalization of Ti3C2Tz. XRD, EDS, and XPS measurements confirm the removal of much of the terminal groups of ML-Ti3C2Tz. Here, the annealed ML-Ti3C2Tz was refunctionalized by -OH groups and 3-aminopropyl triethoxysilane (APTES), which was confirmed by FTIR. The -OH and APTES surface-modified ML-Ti3C2Tz are evaluated as a solid lubricant, exhibiting ∼70.1 and 66.7% reduction in friction compared to a steel substrate, respectively. This enhanced performance is attributed to the improved interaction or adhesion of functionalized ML-Ti3C2Tz with the substrate material. This approach allows for the effective surface modification of MXenes and control of their functional properties.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.