Microstructure evolution, strain-induced martensite transformation (SIMT) kinetics, tensile properties, deformation behaviors of UNS S32101 duplex stainless steel (DSS) with heterogeneous layered structure (HLS) were investigated. HLS composed of multiscale grains (spanning coarse, fine, and ultrafine grains) was prepared by direct cold rolling in combination with short-time annealing, being dominated by coarse-grained ferrite (CGed α) and fine-grained austenite (FGed γ). A quantitative SIMT kinetics model was established to predict the α′-martensite fraction at various strain/annealing parameters, indicating that increased average grain size (AGS) for γ not only contributed to the SIM formation but also promoted the monotonic increase of SIMT rate until annealing for 10 min. Relatively high stacking fault energy (SFE, 35.89∼39.34 mJ/m2) favored mechanical twinning as the dominant deformation mode of γ accompanied by SIMT and dislocation glide. And α deformation was mainly coordinated by wavy slip. Both SFE and Olson-Cohen parameters were strongly correlated with the γ AGS, which could reasonably interpret the dependence of SIMT on the AGS. The A and B values increased progressively with grain coarsening along with the rapid decline in SFE, facilitating the martensite formation. Further increasing the AGS beyond the peak region severely suppressed SIMT probably due to the low probability of martensite embryo generation at deformation twins (DTs) intersections, coinciding with the sharp decrease A value.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.