Abstract
Thick films of NiO deposited on glass substrate by screen printing technique. The nano powder of AR grade NiO was used for the preparation of thick films. The X-ray diffraction (XRD), Scanning Electron Microscopy and Electrical Characterization was carried out for unannealed and annealed films. The annealed films were at 250 0 C-400 0 C in a muffle furnace. Using characterisation techniques, the success of the synthesised nanoparticles was confirmed. The x-ray diffraction was used for structural characterization which confirms the polycrystalline nature of the films with cubic structure. From the SEM analysis the films show uniformity, roughness, large crystals and agglomeration of particles. The SEM-EDS analysed morphology and chemical compositions. The correlations between structural and morphological properties are reported. The D.C. resistance of the films was measured by half bridge method in air atmosphere at 30OC to 350OC. From the electrical parameters the NiO films shows semiconducting nature. The TCR, activation energy and sheet resistivity, specific surface area were calculated at different annealing temperatures. The electrical conductivity at room temperature was calculated as 4.56 × 𝟏𝟎 −𝟒 (𝜴 ∙ 𝒎) −𝟏 .
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
More From: International Journal of Innovative Technology and Exploring Engineering
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.