Abstract
A perovskite type of (La,Sr)MnO/sub 3/ films were deposited on SiO/sub 2//Si substrates with amorphous surface by using the facing targets sputtering apparatus. Although the film as-deposited at P(O/sub 2/) of 0.3 mTorr was not fully crystallized and the MR ratio was as small as 0.03% at the applied field of 5 kOe, it increased up to 2.5% for the film post-annealed at 850/spl deg/C in air for 10 min. The partial O/sub 2/ pressure P(O/sub 2/) strongly affected their crystallinity as well as the Mn content C/sub Mn/. The film as deposited at P(O/sub 2/) of 0.03 mTorr was composed of crystallites with excellent (100) orientation at relatively low substrate temperature T/sub s/ up to 500/spl deg/C and the large MR ratio of 3.8% was attained even at room-temperature measurement. Since this MR response exhibits excellent linearity, these LSMO films seem to be applied for magnetic sensor devices. It is clarified that the annealing process in preparation of LSMO film effectively increases the MR ratio of the film with insufficient crystallinity, and is not effective for the fully crystallized film.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.