Abstract
AbstractIn this study, we investigated the influence of isothermal treatment of poly(lactic acid) (PLA) 3D printed samples at different crystallization temperatures. In this case, we analyzed the effect of each crystallization temperature on spherulites formation in printed PLA, affecting the final mechanical properties of pieces. For such, the thermomechanical properties, morphological structure, and crystallization kinetics were analyzed before and after thermal treatment. The 3D printed samples were heat treated at 80°C, 90°C, 100°C, 110°C, and 119°C. With annealing, we observed an improvement in the mechanical PLA properties; however, the exothermic crystallization peak was different for the samples. Pieces before annealing were found to have a low crystallinity index (Ic) of 2%–7%, and the pieces after annealing presented a considerable Ic (27%–34%). Annealing temperatures of 100°C, 110°C, and 119°C produced the fastest crystallization kinetics, while annealing temperatures of 80°C and 90°C resulted in the lowest crystallization kinetics for complete crystallization. After annealing, improvement in the flexural strength (34%–47%) and Young's modulus (26%–51%) for all annealed pieces occurred. The appropriate condition was observed at 100°C, which was the onset temperature of crystallization, owing to the combination of the shorter time of crystallization with the increased mechanical properties.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.