Abstract
In the present work it has been studied the effect of microstructure on tensile properties of semi-continuously cast round billets manufactured in the industrial 6063 alloy either in the as cast state or after heat treatment. Relevant microstructural features were characterized by quantitative metallographic techniques, both in the periphery and centre of billets, and contrasted against the measured tensile properties at room temperature. Special attention in the study was paid to the way in which chemical non-homogeneities could be minimized. For such purpose the refinement and shape modification of second phase particles formed during solidification, thereafter transformed during the subsequent industrial heat treatment, were assessed. It was observed that the morphology of iron-rich intermetallic compounds developed during solidification was highly influenced by the solidification rate as seen in the billet cross section. It was also verified that the optimal elongation corresponded to the central portion of the billet once industrially homogenized.
Highlights
En el presente trabajo se analiza el efecto que tienen sobre las propiedades mecánicas en tracción, las diferencias microestructurales entre la superficie y el núcleo de lingotes de la aleación industrial 6063
In the present work it has been studied the effect of microstructure on tensile properties of semi-continuously cast round billets manufactured in the industrial 6063 alloy either in the as cast state or after heat treatment
Relevant microstructural features were characterized by quantitative metallographic techniques, both in the periphery and centre of billets, and contrasted against the measured tensile properties at room temperature
Summary
Las aleaciones de aluminio han sido clasificadas por la American Aluminium Association (AAA) en diferentes series, según los elementos de aleación que las constituyan. La resistencia a la corrosión, la capacidad de endurecimiento estructural o el buen comportamiento frente al mecanizado son algunas de las características que pueden verse afectadas por la segregación en los bordes de los granos. Sin embargo en estado bruto de moldeo, estas aleaciones no son adecuadas para los procesos de conformado en caliente mediante extrusión, laminación... El tratamiento térmico de homogeneización promoverá la transformación de estas agujas en partículas de menor tamaño y con formas más redondeadas, a-AlFeSi, mejorando la ductilidad del material; provocará además la reducción de la microsegregación de los elementos de aleación y la redisolución parcial de los precipitados de Mg Si, responsables de la dureza potencial del producto una vez conformado[9,10,11]. El estudio ha sido llevado a cabo en una etapa intermedia de la ruta de elaboración de productos conformados por extrusión, tras someter a la aleación al tratamiento térmico de homogeneización
Sign-in/Register to view highlights & summary Sign-in/Register to access full text options 
Free) 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a call