Abstract
The anisotropy of yielding, as measured by the ratio of yield stress in the axial and transverse directions of Zr-2.5Nb pressure tubes used in Canada Deuterium Uranium (CANDU) nuclear reactors, was determined experimentally by testing samples in uniaxial tension. The yield anisotropy was measured in uniaxial tension in samples obtained from the three directions of a Zr-2.5Nb plate and in shear, by testing in torsion “mini” pressure tubes from the same material. From these experiments, the temperature and strain-rate dependence of the yield stress and the dependence of the anisotropy of yielding on temperature were also determined. It is shown that the yield anisotropy of pressure tube material is constant for temperatures up to about 800 K and that the strain-rate sensitivity is also constant up to about 700 K and is equal to ∼0.02. In addition, the activation energy (Q) of this material was estimated by using the temperature dependence and rate sensitivity of the yield stress. It was found to be of the same order of magnitude as that determined earlier by other investigators. A polycrystalline, nonlinear self-consistent model that takes into account the crystallographic texture of the material was used to derive the values of the critical resolved shear stress (CRSS) which are consistent with prismatic, basal, and pyramidal glide and the values of the Hill’s plastic anisotropy coefficients which are consistent with the observed anisotropy of yielding. The model provided an estimate of the complete stress tensor, describing yielding of a Zr-2.5Nb pressure tube material.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have