Abstract
Distribution of the secondary reaction zone (SRZ) on the (1 0 0) plane was investigated in the aluminized Ni-based single-crystal superalloy TMS-75. Preferential formation of the SRZ was observed along the {0 0 1}〈1 1 0〉 directions, whereas the SRZ was not formed along the {0 0 1}〈1 0 0〉 directions. This result can be explained by the anisotropy of recrystallization in the single-crystalline substrate.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callSimilar Papers
More From: Scripta Materialia
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.