Abstract
The microstructure and properties of high strength aluminum alloy under extrusion—hot pressing—solid solution-aging treatment were studied by XRD analysis, hardness and conductivity test, tensile test, intergranular corrosion and exfoliation corrosion test. At the same time, the influence of hot compression technology on the properties of the compressed surface was investigated. The results show that there is anisotropy between the properties of aluminum extrusion-hot pressed material, the hardness and conductivity in the Z direction are higher than those in the X and Y directions, and the tensile strength and plasticity are better than those in the Y direction, among which the strength is increased by about 122 MPa and the elongation by about 6.17%. The corrosion resistance also exists in the anisotropy, in which the Z direction has the best intergranular corrosion resistance and the corrosion depth is 167.46 um, the Y direction has the best exfoliation corrosion resistance and the grade reaches PC grade. The thermal compression process is beneficial to improve the plasticity, electrical conductivity and exfoliation corrosion performance of the compressible surface material, but reduces the hardness, tensile strength and inter-granular corrosion performance.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.