Abstract
The Zr-2.5Nb alloy pressure tubes of Indian Pressurized Heavy Water Reactors were manufactured from double melted ingots initially and subsequently from quadruple melted ingots to reduce impurities such as chlorine, phosphorus and carbon. In the current investigation, creep tests were carried out in the stress range of 0.7–0.9 times the yield strength and the temperature range of 350 °C–450 °C to characterize the thermal creep behaviour of Zr-2.5Nb alloy pressure tubes fabricated from double and quadruple melted ingots. The rupture time, minimum creep rate, stress exponent, activation energy and threshold stresses were obtained by carrying out the creep tests of the samples fabricated with their axis parallel to the axial and transverse directions of the pressure tubes. Experimental analysis revealed that the rupture time for double melted tube was 2–3 times lower than that of quadruple melted tubes, whereas no significant change in minimum creep rate was observed. Stress exponent values were obtained in the range of 3–5 signifying dislocation creep as the dominant creep mechanism. To predict the long-term creep properties, the master curves employing the Larson-Miller and Monkman-Grant methods were also evaluated. The effect of microstructural anisotropy, alloying elements and impurities on the thermal creep behaviour of Zr-2.5Nb pressure tube has been investigated.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callMore From: International Journal of Pressure Vessels and Piping
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.