Abstract
We investigate the effect of direct electric current (DC) on grain growth in 100 nm thick iron-carbon films with carbon concentrations between 0.7 to 4.4 at%. The application of DC-current during annealing at 550 °C confirms the expected transport of carbon in the direction of the electric current and the unexpected formation of elongated, abnormally large carbide and ferrite grains along the current direction in the carbon-rich regions. The formation of elongated grains is explained by electromigration-induced carbon flux divergences that result from the carbide precipitates. This presents a possible scenario for controlling microstructure evolution in iron by using DC electric currents. Changes for alternating current (AC) pulses had been observed before.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.