Abstract
ABSTRACTFracture tests have been carried out for an electroless deposited Ni-P amorphous alloy thin film with different crack growth directions. Cantilever beam type specimens with dimensions of 10 × 10 × 50 μm3 were prepared from a Ni-P amorphous thin film and notches with different directions, which are perpendicular and parallel to the deposition growth direction, were introduced by focused ion beam machining. Fatigue pre-cracks were introduced ahead of the notches. Fracture tests were performed using a mechanical testing machine for micro-sized specimens. Fracture behavior is different between the two types of specimens. As KIC values were not obtained because the criteria of plane strain were not satisfied for this size of the specimen, the provisional fracture toughness KQ values were determined. The KQ value of the specimen with crack propagation direction being perpendicular to the deposition growth direction was 4.2 MPam1/2, while that with crack propagation direction being parallel to the deposition growth direction was 7.3 MPam1/2. This result suggests that the electroless deposited Ni-P amorphous alloy thin film has anisotropic fracture properties.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.