Anisotropic chitosan/tunicate cellulose nanocrystals hydrogel with tunable interference color and acid-responsiveness

Abstract

A robust chitosan/tunicate cellulose nanocrystals (TCNCs) anisotropic hydrogel with bright interference colors was fabricated via combining the prestretching orientation method and chemically-physically dual cross-linking. The oriented regenerated chitosan nanofibrous network enabled the TCNCs alignment by covalent interaction and hydrogen bonding. The stretching alignment endows the chitosan/TCNCs hydrogel with enhanced tensile strength, from 0.63 MPa (draw ratio 1.0) to 2.06 MPa (draw ratio 3.5). Moreover, the orientation of chitosan nanofibers led to birefringence appearance, which could be regulated with the TCNCs introduction or draw ratios. The hydrogel swelled completely in 2 min in pH = 3 solution and the interference color disappeared. The oriented chitosan/TCNCs hydrogels showed distinct color change under acid stimulation, which could be quantitatively measured or directly observed under crossed polarizers. This work demonstrated a strategy for fabricating the interference color regulatable hydrogels with acid-response property for sensors and environmental monitoring.