Abstract
The filamentary (Nd 0.333Eu 0.333Gd 0.333) 1.18Ba 2.12Cu 3.09O x superconductors were prepared by solution spinning method and partially melted in flowing 1% O 2+Ar and then oxygenated by a two-step process. The filamentary sample had a dense and well-aligned texture along the diameter as well as the length. The J c of the sample was measured at 77 K in fields up to 10 T. Anisotropic behavior of the J c– B curve along the filament diameter was detected. High J c value of more than 3500 A/cm 2 at 77 K and 10 T was achieved by applying the field in a direction normal to the c-axis of the sample.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.