Anelasticity and relaxation effects in single crystal Mn ferrites

Abstract

Young's modulus and acoustic loss are investigated in three single crystal Mn-ferrites in the 300 to 650 K temperature range. Anelastic behaviour near 500 K is found to be composed of two parts. The first part, strongly dependent on the external magnetic field, is present when acoustic longitudinal vibrations are applied parallel to any of the main crygtallographic axes 〈100〉, 〈110〉 and 〈111〉, respectively. The other part, independent of external magnetic field, is present only with the vibrations along 〈110〉 and 〈111〉 directions. A close analogy of the latter behaviour with the process III, observed in magnetic aftereffect spectra of Mn-ferrites, is found. Der Elastizitatsmodul und der mechanische Verlust wurden in drei Manganferrit-Einkristallen im Temperaturbereich von 300 bis 650 K gemessen. Um 500 K wird unelastisches Verhalten gefunden, welches zwei Effekten zugeschrieben wird. Bin Effekt, der direkt vom angelegten Magnetfeld abhangig ist, erscheint bei longitudinalen Schwingungen parallel zu den drei Kristallrichtungen 〈100〉, 〈110〉 und 〈111〉. Der andere Effekt der Anelastizitat, der unabhangig vom auseren Magnetfeld ist, ist nur bei Schwingungen in der 〈110〉- und 〈111〉-Richtung vorhanden. Er hat eine grose Ahnlichkeit mit dem magnetischen Desakkommodationsprozes III, der in polykristallinen Mn-Ferriten gefunden worden wird.