Abstract

There have been claims of early use of high-carbon steel in South India. Still, the antiquity, elemental composition and steelmaking process have not been explored adequately. The high carbon steel was known in the Iron Age or early historical period. However, the large-scale use of such steel was prevalent only in the medieval times. This article examines the presence of steel and its metallographic features in the iron artifacts retrieved from two archaeological sites, namely Ambal and Vallam, Tamil Nadu, India, with occupational evidence from the Iron Age to the medieval period through a number of scientific tests. Metallographic as well as mechanical tests were performed to identify the morphology and measure the strength respectively. Similarly, the chemical composition was determined to quantify the alloying elements in the material. The slag was exposed on the etched surface of the sample cut from axe. Microscopy and chemical composition analysis showed very fine bright dendrites of wustite in the iron slag. The deterioration of samples was confirmed in microscopic and composition analysis. The result shows that the inhabitants of ancient Ambal and the Vallam were equipped with iron smelting technology and had the knowledge of steelmaking in the Iron Age.

Talk to us

Join us for a 30 min session where you can share your feedback and ask us any queries you have

Schedule a call

Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.