Abstract

In this work, NixCo3-xSy nanoparticles supported by carbon aerogel (CA) were prepared through an innovative hydrothermal and calcining process with the waste watermelon rind as a carbon source, and then the as-prepared NixCo3-xSy/CA composites were performed as an excellent electrode of supercapacitors. The addition of CA substrate can provide abundant reactive sites. For contrast, the electrochemical properties of NixCo3-xSy/CA with different ratios of Ni:Co have been tested. Expectedly, the NiCo2S4/CA hybrid showed the best electrochemical performance. Therefore, a combination of asymmetric supercapacitorcomposed of NiCo2S4/CA as the positive electrode and activated CA (α-CA) as the negative electrode was successfully assembled, wherein α-CA was prepared by using K2FeO4 as the pore-forming agent. The α-CA possessed a three-dimensional (3D) hierarchical porous structure and large specific surface area, thus exhibited an improvement on cycling stability and conductivity. The asymmetric supercapacitor demonstrates a maximum energy density of 33.8 Wh kg−1 at a power density of 800 W kg−1 with a long cycle life of 87.4% capacitance retention after 10,000 cycles at 10 A g−1. This facile, environmentally-friendly, and cost-effective strategy provides more possibilities for the rational fabrication of high-performance supercapacitors.

Talk to us

Join us for a 30 min session where you can share your feedback and ask us any queries you have

Schedule a call

Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.