Abstract
The research focused on the properties of partially fused powder particles and their possible effects on the mechanical and corrosive properties of products produced by Laser Powder Bed Fusion (LPBF). Scanning electron microscopy was used to investigate surfaces and pores, both for adherent particles and for particles completely enclosed in the molten bath. The study focused on Ti-6Al-4V, considering powder particles between 10–45 µm and a layer thickness of 25 µm. Different combinations of laser powers and scanning speeds were chosen to investigate the melting, mixing and solidification behavior. The analysis revealed that certain partially melted powder particles caused microcracks and increased the corrosive surface area, which showed distinct microstructures compared to the core area of the product. The investigation identified fully integrated particles and mostly melted particles by microstructure analysis. The results suggest potential innovative applications in complex product designs where the removal of these particles is a challenge, as well as in bone implantation to improve osseointegration.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.