Analytical electron microscope study of the omega phase transformation in a zirconium--niobium alloy

Abstract

An in-situ study of the as-quenched omega phase transformation in Zr--15% Nb was conducted between the temperatures of 77 and 300/sup 0/K using analytical electron microscopy. The domain size of the omega regions observed in this investigation was on the order of 30 A, consistent with previous observations in this system. No alignment of omega domains along <222> directions of the bcc lattice was observed and in-situ thermal cycling experiments failed to produce a long period structure of alternating ..beta.. and ..omega.. phase regions as predicted by one theory of this transformation. Several techniques of microstructural analysis were developed, refined, and standardized. Grouped under the general classification of Analytical Electron Microscopy (AEM) they provide the experimentalist with a unique tool for the microcharacterization of solids, allowing semiquantitative to quantitative analysis of the morphology, crystallography, elemental composition, and electronic structure of regions as small as 20 A in diameter. These techniques have complications, and it was necessary to study the AEM system used in this work so that instrumental artifacts which invalidate the information produced in the microscope environment might be eliminated. Once these factors had been corrected, it was possible to obtain a wealth of information about the microvolume of material under investigation. The microanalytical techniques employed during this research include: energy dispersive x-ray spectroscopy (EDS) using both conventional and scanning transmission electron microscopy (CTEM, STEM), transmission scanning electron diffraction (TSED), the stationary diffraction pattern technique, and electron energy loss spectroscopy (ELS) using a dedicated scanning transmission electron microscope (DSTEM).