Abstract
Welding crack analysis was carried out on tee joint crack of boiler platen superheater header (12Cr1MoV) of subcritical power station applying finite element analysis,microanalysis, mechanical properties test, chemical composition analysis, metallography examination and SEM observation etc. Results indicated that the improper structure, the original welding defects, higher welding heat input, excessive welding residual stress and improper heat treatment led to cold crack and reheat crack ,then induced to the leakage failure while operating.the welding crack originated at the original defects, connected with reheat cracks during propagation and led to leakage finally.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.