Abstract
The deoxidation of steel melted using various types of deoxidizers during out-of-furnace treatment is studied. The total oxygen and nitrogen content and the oxygen contents in the main types of oxide nonmetallic inclusions are determined by fractional gas analysis of steel samples taken from heats performed by various schedules. The main types of nonmetallic inclusions and their size distributions are found with qualitative and quantitative metallography. The oxygen content in the rail steel is minimal (5 ppm) when calcium carbide CaC2 is introduced into the metal in tapping of a converter. When the metal is deoxidized using a steel wire filled with calcium or a steel wire filled with silicocalcium, the oxygen content in rail steel is ≈8 and ≈11 ppm, respectively. A comparison of various processes of rail steel deoxidation under the OAO NTMK conditions shows that the limitation of the aluminum content (no more than 30 ppm) or the use of a wire with a calcium or calcium carbide filler is more effective than the use of a wire filled with silicocalcium.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.