Abstract
The aim of this study was to analyze the flexural strength of ceramics based on yttria-stabilized zirconia (YTZP) , used in the manufacture of dental prostheses infrastructure before and after aging with cyclic fatigue in moisture. The samples were made by pre-sintered blocks of ZirkonTransluzent (Zirkonzahn GMHB) from YTZP ceramics with and without feldspathic ceramic coating, divided into groups: G1 = YTZP control; G2 = YTZP aged; G3 = YTZP + feldspathic; G4 = YTZP + aged feldspathic. The samples were submitted to a three-point bending test with a speed of 0.5 mm / min. The mean values of the flexural strength values were G1 = 645 MPa (DP ± 124), G2 = 681 MPa (DP ± 129), G3 = 904Mpa (DP ± 157) and G4 = 954Mpa (DP ± 243). The values of groups G1 and G2; G3 and G4 were statistically similar, depending on the presence or absence of coating. Cyclic stresses did not affect the flexural strength of the material
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.