Abstract
LaFeO3 has been prepared using the solid-state reaction method with High Energy Milling (HEM). The preparation of LaFeO3 was carried out using stoichiometric calculations. Based on the XRD measurement results, single-phase LaFeO3 with an orthorhombic crystal structure was obtained. From the SEM results, the morphology of LaFeO3 is uniform, and the EDS results show the weight percentage of La, Fe, and O elements are 49.74, 21.08, and 29.18 wt%, respectively. VSM LaFeO3 results show magnetic saturation, remanence, and coercivity are 0.24 emu/g, 0.02 emu/g, and 853.38 Oe, respectively, and the absorption of LaFeO3 is -7.40 dB at a frequency of 6.02 GHz with a LaFeO3 sample thickness of 1.5mm.
Published Version
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.