Abstract
Silicone rubber (SR) has the properties of organic–inorganic materials and good adaptability to the space environment, which can be used as an atomic oxygen (AO)-resistant layer on the spacecraft surface. In this study, SR coatings were used to spray on the polyimide surface to prevent atomic oxygen erosion. Then, the physical, chemical, and AO-resistant properties of the SR were investigated. By means of laser diffraction scattering particle size distribution tests, energy-dispersive spectroscopy elemental mapping, and X-ray photoelectron spectroscopy, the fillers and matrix were confirmed as precipitated silica and phenyl SR, respectively. Through analysis of swelling behavior, greater cross-linking density and less swelling ratio were observed at higher temperature and humidity. Furthermore, after AO was exposed with an accumulated fluence of 1.2 × 1021 atoms/cm2, cracks appeared on the coating surface with the change of element content. In addition, it was found that the degree of reaction between AO and SR should not be determined based on mass loss measurements. Our work showed the practical application and great potential of SR protective coating in spacecraft.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.