Abstract
Residual stress profiles were introduced in sodium aluminosilicate glass disks using an ion-exchange process. They were fractured in two loading conditions: indentation and biaxial flexure. The fractal dimension of the macroscopic crack branching pattern called the crack branching coefficient (CBC), as well as the number of fragments (NOF) were used to quantify the crack patterns. The fracture surfaces were analyzed to determine the stresses responsible for the crack branching patterns. The total strain energy in the body was calculated. The CBC was a good measure of the NOF. They are directly related to the tensile strain energy due to the residual stress profile for fractures due to indentation loading. However, in general for materials with residual stresses, CBC (or NOF) is not related to the strength or the stress at fracture, or even to the total stored tensile strain energy. Instead, the CBC appears to be related, in a complex manner, to the distribution of stresses in the body. Therefore, in general, the characterization of the CBC of fractured materials cannot be used to ascertain the prior stress distribution.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.