Analysis of Load Transfer Mechanism in Cu Reinforced with Carbon Nanotubes Fabricated by Powder Metallurgy Route

Abstract

In this research, ductile and high-strength Cu-carbon nanotube (Cu-CNT) composites with different volume fractions of CNTs were fabricated using powder metallurgy route including mechanical milling and hot pressing and microstructure and tensile properties of the resulting materials were studied. Microstructural characterization through scanning electron microscope and quantifying the CNT agglomeration revealed that uniform dispersion of CNTs in Cu matrix decreases with increasing CNT volume fraction. In case of the higher volume fraction of CNTs (i.e., 8 vol.%), ~ 40% of CNTs were observed as agglomerates in the microstructure. Compared to unreinforced Cu, the yield and ultimate tensile strengths increased considerably (about 33% and 12%, respectively) with incorporation of CNTs up to 4 vol.%, but remained constant afterward. Meanwhile, the elongation decreased from 15.6% for Cu to 6.9% for Cu with 8 vol.% CNT. The relationship between the change in yield strength of the composite and the microstructure was investigated using analytical models. The results showed good consistency between calculated and measured data when the negative effect of CNT agglomerates in the models were taken into account.