Abstract
In this study, to clarify the unknown physical properties of the Mg-Al-Th-RE alloy, the relationship between the injection conditions and the internal porosities, and the mechanical properties exerted by the solidification microstructure was investigated. The obtained cast samples were investigated using X-ray CT internal measurements, tensile tests, Vickers hardness tests, and solidification microstructure observations. The tensile strength and the elongation at the injection speed of 5.0 m/s were higher than at 2.0 m/s. The number of porosities affected the tensile strength and the elongation even at the same fracture position. In addition, it was confirmed that segregation affected the destruction smaller the porosity size and the greater the variability of porosity. As the injection speed increased, the amount of heat transferred between the molten metal and the wall surface also increased, resulting in quick freezing and solidification. The tensile strength increased at the injection speed of 5.0 m/s because the interface between the scattered primary crystals and eutectic systems was narrow. On the other hand, at the injection speed of 2.0 m/s, the tensile strength decreased because the molten metal was delayed in solidification and dendrite growth became remarkable.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.