Abstract
Folding cracks of linerboards in relation to their micro-elongation and the forming conditions were studied using an industrial linerboard machine with a top former. The experiments consisted of the study of various forming conditions by manipulating the jet/wire speed ratio to produce linerboard with differences in fiber structures that were related to the cracked and uncracked products. The results showed that changes to the jet/wire speed ratio of about 0.01–0.02 to improve the tested folding endurance in the machine direction potentially produced folding cracks in the linerboard, which indicated an ambiguous interpretation of the foldability tests. The delaminated cracked layers were found to have a high folding endurance and tensile strength, while the decrease in the micro-elongation formulated in this study was found to be related to cracking. A lower micro-elongation of about 350–500 μm/N·g was found in a range of products with folding cracks.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.