Abstract
YCr 0.5 Mn 0.5 O 3 (YCM)-CaCu 3 Ti 4 O 12 (CCTO) ceramics were prepared using a solid processing method, and their properties were studied. XRD measurements showed that all prepared ceramics had pure perovskite structures. With increasing YCM content, grain size in ceramics decreased, and the resistivity of materials was found to be very sensitive to grain size and grain size distribution. Moreover, ceramics had NTC characteristics, and values of ρ 25 , B 25/75 , and E a ranged from 2.21 × 10 6 –7.30 × 10 6 Ω cm, 5797–6300 K, and 0.5390–0.5800 eV, respectively. The presence of heterovalent ion pairs in samples suggested that conduction mechanism may have been related to electron hopping. Impedance spectroscopy results showed that excessive doping with YCM resulted in greater contribution from grains to overall resistance of the material. Temperature-dependent electrical relaxation behavior was dominated by short-range movement of charge carriers.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.