Abstract
A CMSX-4 3-point bend specimen was statically loaded under hot corrosion conditions and SEM, (S)TEM and EDX techniques were used to analyse the cracking generated. Sulphur, chlorine, sodium and oxygen were found at the crack tip, and an influence of loading on the corrosion mechanism’s preference to interact with either the γ or γʹ was observed. The microscopy analysis is in support of the corrosive mechanism being a combined stress and electrochemical corrosion linked with low temperature hot corrosion, where crack propagation occurs as a result of localised corrosion enhanced material degradation. High magnification EDX mapping identified W as segregating to the γʹ at room temperature.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callSimilar Papers
More From: Corrosion Science
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.