Abstract
The microstructure of a new martensitic high-strength steel (Fe-0.40C-3.81Ni-1.31Cr-1.50Si-0.75Mn-0.52Mo-0.51Cu-0.30V) with high fracture toughness is characterized by transmission electron microscopy and atom probe tomography (APT). MC, M6C, and M23C6 precipitates form inside the martensitic lath matrix. The fracture toughness is insensitive to the dissolution of M23C6 precipitates at austenitizing temperatures above 1164 K (891 °C). APT reveals that solute segregation at the prior austenite grain boundaries (PAGB) is not uniform, with C, Mo, Si, Ni, and/or P enrichment varying at different areas of the PAGB. Si depletion is detected in the same area as the highest C enrichment. Carbon also segregates at lath boundaries. Segregation of C indicates the presence of retained austenite films at both PAGB and lath boundaries. Regions enriched in C up to 10 pct were found within the laths; however, no regions were enriched to the level expected of cementite or e-carbide. The observed C distribution and high fracture toughness indicates that the tempering behavior is significantly different than that observed in 300M steel. The effect of Si, Ni, and Cu on the formation and stabilization of the regions of C enrichment and retained austenite require further study, as it may be key to the increased toughness.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.