Abstract
The paper analyzes the wear and durability of abrasive films designed for microsmoothing produced by electrostatic method. In order to carry out tool wear studies, a microgrinding process was performed using an abrasive film with a nominal grain size of 15 μm. The next step was the study, using scanning microscope. Crushed grains were observed on the surface of the foil, overflows, and extremely high temperatures in the treatment zone, above 1400°C, which resulted in the formation of spherical chips.
Highlights
The paper analyzes the wear and durability of abrasive films designed for microsmoothing produced by electrostatic method
In order to carry out tool wear studies
a microgrinding process was performed using an abrasive film with a nominal grain size of 15 μm
Summary
The paper analyzes the wear and durability of abrasive films designed for microsmoothing produced by electrostatic method. Charakterystyczne cechy procesu to jednokrotne wykorzystanie narzędzia oraz bardzo długie ślady obróbkowe, co jest wynikiem nawet 1000-krotnie wyższej prędkości przedmiotu obrabianego w porównaniu z prędkością przemieszczania się folii ściernej [3, 4]. Podczas wytwarzania folii mikrościernych typu IMFF proces osadzania ścierniwa (elektrokorundu szlachetnego) na powierzchni nośnika (folii poliestrowej) pokrytego warstwą spoiwa podstawowego odbywa się metodą elektrostatyczną Obraz SEM powierzchni folii ściernej typu IMFF o nominalnym rozmiarze ziarna 15 μm tzw. Metoda elektrostatyczna osadzania ziaren ściernych na powierzchni nośnika zapewnia takie zorientowanie ostrzy skrawających, aby uzyskać korzystną topografię powierzchni czynnej narzędzia
Sign-in/Register to view highlights & summary Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.