Abstract
In this work, DIFT technology and Q&P process were combined in order to introduce ultrafine-grained ferrite into the matrix of martensite and retained austenite to develop a new kind of advanced high strength steel, and two kinds of steels were investigated by this novel combined process. The newly designed process resulted in a sophisticated microstructure of a large amount of ferrite(about 5 μm in diameter), martensite and a considerable amount of retained austenite for TRIP 780 steel. The ultimate tensile strength can reach about 1200 MPa with elongation above 16% for TRIP 780, that is much higher than the one solely treated by Q&P process. Tensile tests showed that both steels with the novel combined process achieved a good combination of strength and ductility, indicating that the new process is promising for the new generation of advanced high strength steels.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.