Abstract
Underfilling is the preferred process to reduce the impact of the thermal stress that results from the mismatch in the coefficient of thermal expansion (CTE) between the silicon chip and the substrate in Flip Chip Packaging. Voids formation in underfill is considered as failure in flip chip manufacturing process. Voids formation possibly caused by several factors such as poor soldering and flux residue during die attach process, voids entrapment due moisture contamination, dispense pattern process and setting up the curing process. This paper presents the optimization of two steps curing profile in order to reduce voids formation in underfill for Hi-CTE Flip Chip Ceramic Ball Grid Array Package (FC-CBGA). A C-Mode Scanning Aqoustic Microscopy (C-SAM) was used to scan the total count of voids after curing process. Statistic analysis was conducted to analyze the suitable curing profile in order to minimize or eliminate the voids formation. It was shown that the two steps curing profile provided solution for void elimination.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.