Abstract
The writer successfully obtained brazed Cu-Al joint by using vacuum brazing method, and also conducted an analysis for the microstructure morphology of the joint. The result shows that: The interface of the brazed Cu-Al joint includes three parts---the transition area on the Cu side, the central brazing seam area and the transition area on the Al side. Formed between the brazing seam area and the Cu substrate are the Cu3Al2 and CuAl2 layers, and the average width of the transition area of Cu3Al2 is 12 μm while that of CuAl2 8 μm. The brazing seam area is mainly composed of α-Al solid solution, Cu3Al2 and CuAl2 metal compounds, in addition, the ε-Cu15Si4 phase, the Al-Si phase and CuZn2 phase are also formed. These phases present themselves in the state of acicular compounds, which are dispersed in the brazing seam area.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.