An investigation on the possibility to improve the corrosion and cavitation resistance of SS304 steel by NiTi coatings

Abstract

Equiatomic and near equiatomic NiTi alloys, showing good mechanical and thermal shape memory properties, are widely exploited in different industrial applications. In addition, NiTi alloys have promising anti-cavitation and corrosion-resistance properties. These advantages have provided opportunities to exploit NiTi alloys as the coatings for protecting materials used in the industrial applications. This study is a preliminary investigation aiming to evaluate the feasibility to form NiTi alloy coatings on SS304 steel by tungsten inert argon arc welding (TIG) technology. The microstructure analysis shows that the crystalline phases in NiTi coatings on SS 304 steel are TiNi-B2, TiNi-B19’ and Ni3Ti. The potential of the NiTi coatings to enhance the corrosion resistance and cavitation resistance behaviors of steel exposed to seawater is studied. NiTi coatings, with two different thicknesses of about 1.2 and 2 mm, having homogenous microstructures were successfully deposited on SS304 steel using TIG technology. Results of tests, done in aqueous solutions simulating seawater, showed that the formation of the oxide films on the surface of NiTi coatings increased the corrosion resistance and wear resistance and decreased the damage caused by the cavitation. Moreover, it was understood that the NiTi coatings with 2 mm in thickness show the superior performances than those with 1.2 mm in thickness. The tribological mechanisms responsible for the unique properties of NiTi alloy coatings were investigated. The wear-resistance behaviors of NiTi alloy coatings are greatly influenced by the friction conditions. Increasing load decreased CoF and the wear rate of the coatings were almost constant, which was attributed to the pseudoelasticity of NiTi alloy. The attractive properties of NiTi alloys that makes it most influential materials for industrial applications have also been discussed.